Private on-device repair evidence
Gaps Between First-Layer Lines
A detailed STLBEAST repair guide to close visible gaps without crushing the first layer. Learn how to recognize the symptom, rank the likely causes, apply safe fixes in order, verify the result, and prevent the failure from returning.
Not started0 of 8 stepsNot yet saved

Record the setup that produced this result
Saved only in this browser with the repair. Nothing is uploaded.
Add before and after photos for this report
Photos stay in this open page only and are never stored or uploaded. They appear in the printed report while the page remains open.
Controlled test history
No controlled tests have been logged yet. Return to Workshop Mode and record each change before running another test.
Step completion
- 1Document the failure and confirm that it matches this guide: Separate lines leave the build surface visible between passes.Not completed
- 2Return extreme overrides to a known printer, nozzle, material, and slicer profile so the diagnosis starts from a stable baseline.Not completed
- 3Check z offset too high. Lower Z offset slightly.Not completed
- 4Check first-layer flow too low. Return first-layer flow to baseline.Not completed
- 5Inspect nozzle restriction. Check extrusion consistency.Not completed
- 6Rule out incorrect line width profile. Verify line width and nozzle size.Not completed
- 7Change only the single setting or hardware condition supported by the evidence, then run a small test that reproduces the original failure.Not completed
- 8Compare the test against the target condition, record the successful value, and save it in a printer/material profile before repeating the full print.Not completed
Observations and winning values
No notes recorded.
Verification test
- Model
- Single-layer five-zone test
- Setup
- Use the final plate, material, mesh and first-layer profile.
- Pass
- Lines join evenly in the centre and corners, with no scraping, gaps or lifting.
- If unchanged
- One or more zones remain loose, transparent, ridged or detached.